Incoloy 901
Description:
Alloy 901 is an age-hardenable super alloy which contains Titanium and Aluminium for precipitation hardening and molybdenum for soild-solution strengthening. Alloy 901 has high yield strength and creep resistance at temperatures to about 1110°F (600°C). As Alloy 901 has a substantial iron content it enables alloy 901 to combine strength with good forging characteristics. Alloy 901 is commonly used for gas turbine engine discs, shafts, rings, casings and seals.
Chemical Composition:
Element |
Content (%) |
Nickel, Ni |
40-45 |
Iron, Fe |
33 |
Chromium, Cr |
11-14 |
Molybdenum, Mo |
5.0 - 6.50 |
Titanium, Ti |
2.80-3.10 |
Cobalt, Co |
1 |
Manganese, Mn |
0.50 |
Copper, Cu |
0.50 |
Silicon, Si |
0.40 |
Aluminum, Al |
0.35 |
Carbon, C |
0.10 |
Sulfur, S |
0.030 |
Mechanical Properties:
Properties |
Metric |
Imperial |
Tensile strength (precipitation hardened, value at room temperature) |
1200 MPa |
174000 psi |
Yield strength (@strain 0.200%, precipitation hardened, value at room temperature) |
875 MPa |
127000 psi |
Elongation at break (precipitation hardened) |
15% |
15% |
Specifications:
l UNS N09901
l Werkstoff Number 2.4662
l BR HR 55
l AMS 5660
l AMS 5661
l AECMA PrEN2176
l AECMA PrEN2177
l ISO 9723
l ISO 9725
l MSRR 7029, MSRR 7031
l Nimonic alloy 901