Mumetal 80
Description:
Magnetic Shielding Alloy Mu-Metal / HY-MU 80
Mumetal is 80% nickel with additions of iron and molybdenum as main elements in turn this alloy offers an extremely high initial permeability. It is only moderately resistant to moisture and atmospheric corrosion, it used mainly in in transformer cores but is well known for its magnetic properties which are used for shielding electrical components from magnetic fields. "HYMU 80" has a minimum DC permeability of 80,000 at a flux density of 40 gauss when heat treated by the recommended procedure and test in accordance with ASTM 596.
Chemical Composition:
|
Weight% |
Ni |
Cu |
Cr |
S |
P |
Si |
Mn |
C |
Mo |
Fe |
|
Hymu 80 (Comp1) |
79.0-80.6 |
|
|
0.008 |
0.02 |
0.42 |
0.95 |
0.03 |
3.8-5 |
Rem |
|
MIL N 14411C (Comp2) |
75.0-77.0 |
4.0-6.0 |
3.0 |
0.02 |
0.02 |
0.50 |
1.8 |
0.05 |
|
|
Specifications:
l Permalloy
l HYMU 80
l MAG 7904
l MIL N 14411 C, COMP. 1
l ASTM A753-78 and ASTM 596
Mechanical Properties:
|
Yield Strength (psi) |
Tensile Strength (psi) |
Elongation in 2" (%) |
|
44,000 |
100,000 |
40 |
Physical Properties (Annealed Condition):
l Specific Gravity - 8.7g/cm
l Curie Temperature - 830°F (410°C)
l Electrical Resistivity, 349 ohm circ mil/foot 0.55 ohm mm2m
l Density lb/cu.in. - 316
l Thermal Conductivity - 134 btu-inch/ft hour °F 0.32 W/cm °C
l Coefficient of Thermal Expansion, in./in. °F x 10 (-******)
l 7.2in/in °F x 10-6 between 70 and 400F
l 13cm/cm/ °C 10-6 between 30 and 204 °C