Maraging 300
Description:
Maraging 300/Udimar 300/Maraging C300/UNS K93120/UNS K93160
Maraging 300 alloy steels material (also referred to as Maraging C300 and Vascomax C300) is a vacuum induction melted and vacuum arc re-melted, low-carbon, nickel-cobalt-molybdenum high-temperature nickel alloy. This material can produce yield strengths in excess of 270 ksi (1862 MPa) through simple, low-temperature heat treatment at 900°F (482°C). Maraging steel 300 also exhibits good ductility at high strength levels, displays excellent notch ductility and outstanding weldability.
Maraging 300 is an age hardenable (maraging) iron nickel stainless steel. Maraging 300 has exceptional strength, toughness and is resistant to crack propagation. Maraging 300 is used for tooling, transmission shafts, autosport components and light aircraft landing gear.
Chemical Composition:
Weight% |
C |
Si |
Mn |
S |
P |
Co |
Ni |
Mo |
Ti |
Al |
Fe |
Maraging 300 |
0.03 max |
0.10 max |
0.10 max |
0.010 max |
0.010 max |
8.0-9.5 |
18.0-19.0 |
4.6-5.2 |
0.55-0.80 |
0.05-0.15 |
Bal |
Mechanical Properties:
Material |
0.2 % Yield Strength ksi |
Ultimate Tensile Strength ksi |
Elongation in 4D(%) |
Reduction of Area % |
Hardness HRC |
Maraging 300, Solution Annealed 1500° F (816°C), 1hr, AC |
120 |
150 |
16 |
70 |
30 |
Solution Annealed Plus Aged 900 ° F (482°C), 3 hrs AC |
280 |
290 |
8 |
40 |
52 |
Specifications:
l UNS K93120
l ASTM A579
l AMS 6514 - Bar
l SAE AMS 6514 and AMS 6521 (UNS K93160) - Sheet, Strip, Plate
l MIL S 46850, MIL S 13881
l Werkstoff Nr. 1.6358 and 1.6354
l ASTM A579 Powder
l Also known as Type 300, Maraging 300, C300
l Vdimor 300
l Vascomax C300
Annealing:
Maraging 300 alloy steel can be annealed at 1038°C (1900°F) after cold working and then finally cooled in air.
Cold Working:
Maraging 300 alloy steel can be cold worked by conventional methods.
Welding:
Maraging 300 alloy steel can be welded by conventional methods.
Forging:
Maraging 300 alloy steel can be forged as for stainless 304 alloy.
Forming:
Conventional methods are used to readily form maraging 300 alloy steel that has good ductility.
Machinability:
Maraging 300 alloy steel has good machinability characteristics.
Heat Treatment:
Maraging 300 alloy steel cannot be heat treated for hardening except by aging.
Hot Working:
Maraging 300 alloy steel can be hot worked in temperatures ranging 260 to 93°C (500 to 200°F). Age hardening takes place when this alloy steel is exposed to these temperatures for a long time.
Hardening:
Maraging 300 alloy steel can be hardened by aging and cold working.
Aging:
Maraging 300 alloy steel has high hardness and strength properties and is thus suitable for an aging heat treatment at 482°C (900°F).
Applications:
l Missile & rocket motor cases
l Munitions
l Landing gear components
l Aerospace
l Extrusion tooling
l Die casting
l High performance shafting, gears & fasteners